Mercury Scientific Revolution ASTM Paper

Mercury Scientific Revolution ASTM Paper


W. Brian James


New powder characterization tests such as the rotating drum and the Freeman FT4 rheometer have been introduced in recent years. These instruments have yet to be standardized for use with metal powders. Greg Martiska, Mercury Scientific Inc., presented the results of testing with the Revolution Powder Analyzer and Joe Tauber, Kennametal Inc., presented data from testing with a Granudrum. The third workshop participant was Tim Freeman, Freeman Technology, a Micromeritics company. He presented the test results obtained using the FT4 rheometer.

Louis-Philippe Lefebvre from National Research Council Canada also gave a presentation of work he had performed with an FT4 rheometer, but what he presented is not summarized here. Some of what he presented may be found in the proceedings of the AMPM2019 conference.

Two sets of metal powders were provided to each of the three participants. Samples A, B, and C were Ti-6Al-4V powder and samples X, Y, and Z were SS-316L powder. Both sets of powder had a particle-size-distribution suitable for laser-beam powder-bed-fusion processing. Each set of powders contained virgin powder plus powder that had been cycled through an EOS M290 unit multiple times (with no replenishment with virgin powder)—see Figure 1. At the time of testing, the participants only knew which alloy system the samples were from. They did not know the nature of the other samples in each set.

The objective of the workshop was to see whether the instruments were able to detect quantitative differences between the virgin and recycled powders, and to see how repeatable the test results were. Each participant was requested to run three test repetitions on fresh test portions of powder from each process condition.

It was not the objective of the exercise to comment directly on which powder characteristics are associated with successful performance in any given application. Depending on the outcome of this initial phase of testing, the B09 Standards Committee will decide whether developing a standardized test protocol and proceeding to conduct an inter-laboratory testing program to determine the repeatability and reproducibility of the tests performed using the instruments is worthwhile.

Some characteristics of the powders that were tested are summarized in Tables 1 and 2. The participants did not know these until after they completed their testing—the information was provided after they had presented their findings at the workshop. The “used” powder had been through seven machine cycles while the remaining sample was a 50:50 blend of the virgin and used materials.

Secondary electron images of the virgin and used powders are shown in Figures 2 and 3. A more detailed characterization of the powders was subsequently presented by Tony Thornton, Micromeritics, at POWDERMET2019 and is published in the conference proceedings, Advances in Powder Metallurgy & Particulate Materials 2019.1 This summary will be divided into two parts. The first covers the testing conducted using rotating drums and the second the testing conducted using the FT4 rheometer. ROTATING DRUM TESTS Revolution Powder Analyzer The Revolution Powder Analyzer (Figure 4) uses a rotating drum with borosilicate glass sides to measure the flowability potential of powders. The operator starts the flowability test by placing a 100 cm3 test portion of the powder into the drum (other drum sizes are available). A motor rotates two high-precision rollers that in turn rotate the drum. A digital camera, with the assistance of cold-cathode back-light illumination takes digital images of the powder during the rotation process. From the images collected, the software measures the behaviour of the powder due to the drum rotation and how this behaviour changes over time. The digital camera captures images of the powder in the rotating drum at the specified rotation speed. The three images displayed in Figure 5 represent an avalanche cycle from initial image, peak, and the completed avalanche. Images are collected and processed at a high frame rate to capture the exact motion of the powder sample. Samples were tested on the Revolution Powder Analyser using the flow test to study low-speed flowability (how powders flow in the avalanching or slip-stick regime), the packing test to study vibrational packing and consolidated flow (how powders respond to vibration and how they flow after consolidation), and the multi-flow test for high speed flow (how powders transition from avalanching to continuous flow as their flow speed increases). The complete sequence of testing for each test portion took approximately 15 minutes. DYNAMIC FLOW TESTING For the dynamic flow test, 100 cm3 test portions were placed in the test drum and the drum was loaded into the Revolution Powder Analyzer. The flowability test was conducted at a rotation rate of 0.3 rpm and the frame rate for the test was 20 frames per second. The results for the Ti-6Al-4V and SS-316L powders are summarized in Table 3, and the repeatability of the tests is reported in Tables 4 and 5 for the Ti-6Al-4V and the SS-316L powders respectively.

The avalanche energy is the amount of energy released by an avalanche in the powder test portion. It is calculated by subtracting the energy level of the powder after an avalanche from the energy level before the avalanche. The reported avalanche energy is the average avalanche energy for all of the powder avalanches.

The break energy is the maximum energy level of the powder test portion before an avalanche begins. This energy level or force represents the amount of energy/force required to start each avalanche. The reported break energy is the average break energy for all of the powder avalanches.

For every digital image taken, the software measures the density of the sample. The software then calculates the average density (dynamic density) of the powder during the test.

The software collects the angle of the powder at the position of maximum energy prior to the start of the powder avalanche occurrence. The reported value for the avalanche angle is the average value for all the avalanche angles. For the avalanche cycle depicted in Figure 4, the avalanche angle would be calculated at the peak cycle. The software calculates the flowability angle from the centre point on the powder edge to the top of the powder edge.

The yield strength is the average of the shear stresses created when the test portion starts to flow.

The cohesion-T or thickness cohesion is the average of the shear stress created by the thickness of the flowing layer in the test portion as the powder moves between the point where it starts to flow and when it stops flowing. The shear stress is calculated using the thickness of the flowing layer, the density of the powder bed, the volume fraction of the powder bed, and the angle of the powder bed.

For both the Ti-6Al-4V and the SS-316L powders, the used powders had the best low-pressure flow properties with the lowest avalanche energy, break energy, avalanche angle, yield strength, cohesion-T, and surface fractal. The used powders also had the highest dynamic density. This is typical, as samples that flow better usually allow particles to flow around each other better and fill the air spaces between the particles more efficiently. The excellent repeatability of the tests is apparent from the data summarised in Tables 4 and 5.


With the same test portion in the drum that was used for the dynamic flow test, the drum was rotated at 20 rpm for 10 seconds to condition the test portion for the packing analysis test. Images were then taken to calculate the volume of the test portion after conditioning. The powder was then vibrated at 100 Hz at a vibration amplitude of 6.4 mm for 15 seconds and after vibration an image was taken to calculate the new volume of the test portion. The powder was then rotated at 2 rpm until the compacted powder broke (or avalanched). The software captured the angle when the powder broke and the amount of drum rotation required to break the powder, and then calculated the energy needed to initiate flow in the test portion. The digital camera recorded images of the powder after preparation (conditioning), after vibration, and prior to the powder break as seen in Figure 6.

The results of the packing tests are summarized in Table 6.

For both the Ti-6Al-4V and SS-316L powders, the used test portions had the lowest volume change and break angle. All test portions showed a significant increase in density due to vibration but all had little memory of the compression once they flowed again. All test portions had an increase in the strength required to initiate flow compared with samples already flowing. This is indicated by the increase in the maximum break angle compared with the avalanche angle from the dynamic flow test.


For the multi-flow test the test portions were rotated at speeds from 1 rpm to 16 rpm (1 rpm, 4 rpm, 7 rpm, 10 rpm, 13 rpm, and 16 rpm). The frame rate for these tests was 40 frames per second. The results are summarized in Table 7 for both the Ti-6Al-4V and SS-316L powders.

The used test portions had the best flow properties across different flow speeds. They also had the highest volume fraction. The effect of rotational speed on selected properties is illustrated in Figures 7–12. The repeatability of the multi-flow test results can be seen from Tables 8 and 9.


The Granudrum (Figure 13 ) is similar in principle to the Revolution Powder Analyser. The specific equipment used is, however, slightly different and the algorithms used to analyse the data are also different.

For the tests conducted using the Granudrum, 50 cm3 test portions were used. Tests were conducted at 1 rpm and the rotational speed was then increased to 5 rpm and then in increments of 5 rpm up to a rotational speed of 60 rpm. Measurements were made at each rotational speed as the speed of rotation was increased and also when the speed was decreased. Fifty digital images were taken for each increasing and decreasing rotational speed. The results obtained are summarised in Figures 14–17.

At low rotational speeds (40 rpm it appears that the powders start to cataract at the top of the drum making measurements questionable. Under these conditions, a portion of the powder is free falling and not in contact with the powder bed, and at this point, the powders do not have a flow angle nor do they have a flowing layer. It is hard to see the cataract in the powder bed when looking at a back-lit grey scale image (Figure 18). However, when both front and back lighting are compared, the cataract is clearly visible when the drum is lit from the front (Figure 19).


The Revolution Powder Analyzer was able to discriminate between the various test portions and had very repeatable data. It therefore appears worthwhile to continue testing with this equipment to determine how reproducible (testing at various laboratories) the results are. The Granudrum, however, was unable to discriminate on the basis of flow angle and the cohesive index data for the virgin and used powders only differed at rotational speeds where the powder was cataracting and where measurements are questionable. For the Ti-6Al-4V powder the 50:50 blend could not be distinguished from the used powder, and for the SS-316L powder the blend could not be distinguished from the virgin powder. It is clear that there are differences between the two rotating drum units and this will need to be addressed if and when a standardized test method is written—ensuring that the conditions required to achieve good data are satisfied.


The Freeman FT4 rheometer is described as a universal powder tester. It was developed originally to characterize the flow properties of powders and this is still a primary function of the instrument. Accessories and methodologies have been added, however, such as a shear cell to measure a powder’s shear strength, a wall friction kit to quantify how the powder shears against the wall of the process equipment, plus means to measure bulk properties such as density, compressibility and permeability. In this article, emphasis will be placed on the dynamic measurements. The FT4 rheometer is shown in Figure 20 and the principles of the dynamic measurements illustrated in Figures 21 and 22. The rheometer measures the resistance of the powder to flow whilst the powder is in motion. A precision blade is rotated and moved downwards on a helical path through the powder to establish a precise flow pattern. The resistance experienced by the blade is measured both on the downward as well as the upward motion of the blade. The instrument measures both rotational and vertical resistance and it is the composite of the two signals that quantifies the total resistance of the powder to flow. A conditioning step is performed prior to any testing. The results of dynamic measurements for both the Ti-6Al-4V and SS-316L powders are summarized in Table 10. The tests were carried out using a 23.5-mm blade and a 25-mm diameter vessel.

Basic flow energy (BFE) is the energy required to establish a particular flow pattern in a conditioned, precise volume of powder. The flow pattern is a downward anti-clockwise motion of the blade that generates a compressive, relatively high stress flow mode in the powder. The BFE is calculated from the work done in moving the blade through the powder from the top of the vessel to the bottom—i.e., during the downward traverse.

The basic flowability energy (BFE) for the SS-316L powder test portions is higher than for the Ti-6Al-4V powders—Figure 23. However, it is not possible to distinguish between the virgin and used powders for either material. The reason for the higher basic flowability energy of the blend is under investigation.

The specific energy (SE) is measured during the upward movement of the blade through the powder.

The flow pattern is identical to that during the downward flow pattern. However, because it is established on the upward traverse and because the powder is now unconfined, i.e., the powder can lift up, the energies measured are more dependent on inter-particular forces and less influenced by other factors such as compressibility (such as in the BFE test—powder is confined and can’t move down due to the base of the vessel).

The specific energy (SE) of the used powders was lower than that of the virgin powder for both the Ti-6Al4V and SS-316L materials and it is possible to discriminate between the virgin and used powders—Figure 24. The specific energy of the blended powder was higher for both materials and, in the case of the Ti-6Al-4V powder, there was overlap between the SE of the virgin and blended powders.

The stability index indicates whether the flow energy, and therefore the powder itself, is changing as a function of being tested. Particle attrition, segregation, de-agglomeration and de-aeration are examples of what could result in instability.

The stability index values indicate that all of the powders that were tested were physically stable.

The flow rate index measures how sensitive the powder is to being made to flow at different rates through a process by varying the blade tip speed (by a factor of 10).

The flow rate index (FRI) values show minor differences with respect to changes in the flow rate for both materials whether virgin, blended, or used.

Conditioned bulk density (CBD) is calculated automatically using the inbuilt balance of the instrument.

This density is stated to be precise due to the conditioning process that is carried out on the powder before an exact volume of powder is sampled. The conditioning process utilizes the standard blade and moves the powder in a gentle, reproducible way to establish a homogenized stress in the powder. This is stated to be essential for the subsequent measurements, but also for the CBD to be determined.

The CBD of the virgin and used Ti-6Al-4V powders were similar while that of the blended powder was slightly higher. In the case of the SS-316L powders, the used powder had the highest CBD and the virgin powder the lowest.

The presence or absence of air in a powder can greatly affect its flow properties. The addition of air occurs naturally when powder is moved freely, e.g., when discharging powder from a hopper. When aerated, less energy is normally required to move the powder. The aeration behaviour can be represented by the aeration ratio (AR), the factor by which the flow energy is reduced by aeration at a given air velocity—an air velocity of 5 mm/s was used for the tests.

The aeration ratios were significantly higher for the titanium alloy powders compared with those for the stainless steel powders. In the case of the Ti-6Al-4V powders, the used powder had the highest AR suggesting the greatest sensitivity to the introduction of air. The used SS-316L powder had the highest AR for the stainless steel powders.

The aerated energy (AE) is the flow energy measured when air is passed through the powder at a given velocity—in these tests at 5 mm/s.

COMMENTS ON THE FT4 RHEOMETER TESTING The anomalous behaviour, in many instances, of the blended powders in the FT4 rheometer requires further investigation, particularly as the blended powders exhibited values between those of the virgin and used powders for the various tests conducted using the Revolution Powder Analyzer. The inability of the rheometer to discriminate between the virgin and used powders with respect to basic flowability energy is somewhat of a concern. Fortunately, the specific energy (SE) of the used powders was lower than that of the virgin powder for both the Ti-6Al-4V and SS-316L materials and it is possible to discriminate between the virgin and used powders. Nevertheless, in the case of the Ti-6Al-4V powder, there was overlap between the SE of the virgin and blended powders. The various tests with the rheometer require different pieces of equipment, and the full battery of tests needs more time than for the full series of tests run on the Revolution Powder Analyzer. It is, however, likely that additional testing will be carried out using the FT4 rheometer. However, the testing probably will initially be focused on a few of the many possible tests that can be carried out. ACKNOWLEDGEMENTS Thanks to Chris Schade and Dave Cernava of Hoeganaes Corporation for supplying the powder samples for testing and to the companies that participated in the workshop: Greg Martiska of Mercury Scientific Inc., Joe Tauber of Kennametal Inc., Tony Thornton of Micromeritics Instrument Corporation, and Tim Freeman of Freeman Technology, a Micromeritics Company. REFERENCES 1. Tony Thornton, John Guerin, and Jack Saad, The “Effect of the Number of Printer Cycles on Titanium and Steel Powders Used for AM,” Advances in Metal Additive Manufacturing—2019, Metal Powder Industries Federation, Princeton, NJ, 2019.

For more information on  Mercury Scientific Revolution ASTM Paper  talk to  Meritics Ltd

Enquiry Form

More News

Meritics @ Lab Innovations 2018

Meritics @ Lab Innovations 2018

Sustainability and innovation at the heart of the laboratory industry Lab Innovations is the UK’s only event dedicated to the laboratory industry att...

Read More
Smaller Sample volume required for Multisizer Coulter Counter

Smaller Sample volume required for Multisizer Coulter Counter

A new sample handling system from Beckman Coulter reduces minimum volume requirements on the Multisizer 4 COULTER COUNTER Particle Characterization Sy...

Read More
Particle Size Analysis of Coffee

Particle Size Analysis of Coffee

Particle size analysis in the food and beverage sector is concerned with numerous physical phenomena observed in granulated solids, emulsions, liquids...

Read More

Read More

Read More

List your business

Would you like to register your company on one of the UK's largest and most effective Trade websites?

Are you looking for a reliable and consistent source of enquiries from your industry sector? Would you like to see why Find the Needle clients come back year after year to use our service? If so then feel free to register using the link 'here'.

Office Address: